Nickel alloys Manual electrode ENiCrFe-9 Welding makings
KOMPONO KIMIKA:
| ALLOY(wt%) | C | Mn | Si | Fe | Cr | Ni | Mo | Cu | Nb+Ta | |
| GB/T RULA | 0.15 | 1.0-4.5 | 0.80 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0.50 | 0.5-3.0 | |
| NA RULA AWS | 0.15 | 1.0-4.5 | 0.75 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0.50 | 0.5-3.0 | |
| KA WAIWAI LA'ANA | 0.07 | 2.6 | 0.28 | 4.03 | 14.3 | 66.6 | 4.41 | 0.060 | 1.67 | |
WAIWAI MECHANICAL:
| WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | ||||
| GB/T RULA | 360 | 650 | - | 18 | ||||
| NA RULA AWS | - | 650 | - | 25 | ||||
| KA WAIWAI LA'ANA | 460 | 680 | - | 41.5 | ||||
PALAPALA PALAPALA I MANAOIA:
| NĀ KĀNĀWAI (mm) | 2.6*300 | 3.2*350 | 4.0*350 | ||||||||
| UILA (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
| O/W | 55-80 | 65-110 | 80-130 | ||||||||
Haʻahaʻa hydrogen ʻano lima electrode, nominal haku mele (pakeneka ma ke kaumaha) ʻo Ni14Cr4FeNbMo, nickel - chromium - hao hao hao.
Paʻa paʻa, nani ka hana ʻana, liʻiliʻi liʻiliʻi, maʻalahi ka wehe ʻana i ka slag.
ʻO ke kūpaʻa porosity maikaʻi, paʻa nā waiwai mechanical o ka metala hoʻoheheʻe.
-
Nanjing Chengzhi Yongqing Energy 07MnNiMoDR kila ethylene ball tank
Reactor loko
-
Pāhana Arctic LNG-2
KOMPONO KIMIKA:
| ALLOY(wt%) | C | Mn | Si | Fe | Cr | Ni | Mo | Cu | Nb+Ta | |
| GB/T RULA | 0.15 | 1.0-4.5 | 0.80 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0.50 | 0.5-3.0 | |
| NA RULA AWS | 0.15 | 1.0-4.5 | 0.75 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0.50 | 0.5-3.0 | |
| KA WAIWAI LA'ANA | 0.07 | 2.6 | 0.28 | 4.03 | 14.3 | 66.6 | 4.41 | 0.060 | 1.67 | |
WAIWAI MECHANICAL:
| WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | ||||
| GB/T RULA | 360 | 650 | - | 18 | ||||
| NA RULA AWS | - | 650 | - | 25 | ||||
| KA WAIWAI LA'ANA | 460 | 680 | - | 41.5 | ||||
PALAPALA PALAPALA I MANAOIA:
| NĀ KĀNĀWAI (mm) | 2.6*300 | 3.2*350 | 4.0*350 | ||||||||
| UILA (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
| O/W | 55-80 | 65-110 | 80-130 | ||||||||