Nickel alloys Manual electrode ENi-1 weld fabrication makings
KOMPONO KIMIKA:
| ALLOY(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| GB/T RULA | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| NA RULA AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| KA WAIWAI LA'ANA | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
WAIWAI MECHANICAL:
| WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | ||||
| GB/T RULA | 200 | 410 | - | 18 | ||||
| NA RULA AWS | - | 410 | - | 20 | ||||
| KA WAIWAI LA'ANA | 310 | 435 | - | 29 | ||||
PALAPALA PALAPALA I MANAOIA:
| NĀ KĀNĀWAI (mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
| UILA (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Titanium-calcium lima electrode, nominal haku mele (pakeneka ma ke kaumaha) he 95Ni-2.5Ti.
Paʻa paʻa, nani ka hana ʻana, liʻiliʻi liʻiliʻi, maʻalahi ka wehe ʻana i ka slag, kūpaʻa porosity maikaʻi.
Loaʻa i ka metala fused nā waiwai mechanical maikaʻi, ka pale ʻana i ka wela, ka pale ʻana i ka corrosion, ka hui ʻana a me ke kūʻē ʻana.
Hoʻohana nui ʻia nā mea hoʻoheheʻe kila Cr-Mo a me nā mea hoʻoheheʻe electrode surfacing i nā lako hoʻomaʻemaʻe ʻaila.
-
158,000 tona ka mokuahi Suez
Supercore SG
KOMPONO KIMIKA:
| ALLOY(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| GB/T RULA | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| NA RULA AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| KA WAIWAI LA'ANA | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
WAIWAI MECHANICAL:
| WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | ||||
| GB/T RULA | 200 | 410 | - | 18 | ||||
| NA RULA AWS | - | 410 | - | 20 | ||||
| KA WAIWAI LA'ANA | 310 | 435 | - | 29 | ||||
PALAPALA PALAPALA I MANAOIA:
| NĀ KĀNĀWAI (mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
| UILA (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||