Nā huila nikela TIG ERNiCrFe-7A Hoʻohui ʻia
KOMPONO KIMIKA:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T RULA | - | - | - | - | - | - | - | - | - | - |
| NA RULA AWS | 0.04 | 1.00 | 0.50 | 28.0-31.5 | Ua haʻi aku ʻo Rem | 0.50 | 7.0-11.0 | 0.5-1.0 | 0.02 | 0.015 |
| KA WAIWAI LA'ANA | 0.028 | 0.15 | 0.11 | 29.8 | 59.03 | 0.06 | 9.8 | 0.86 | 0.001 | 0.002 |
WAIWAI MECHANICAL:
| WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | Hoʻomaʻamaʻa wela | ||||||
| GB/T RULA | - | - | - | - | - | ||||||
| NA RULA AWS | - | - | - | - | - | ||||||
| KA WAIWAI LA'ANA | - | 760 | 133/Ke wela lumi | 37 | 607°C*25h | ||||||
Nickel-chromium-hao nickel-base alloy kinoea welding uea, nominal haku mele 60% Ni-29% Cr-9% Fe-0.75% Nb.
Maikaʻi nā waiwai metala hoʻoheheʻe ʻia, ʻoi aku ka pale ʻana i ka haʻahaʻa haʻahaʻa plastik (DDC).
ʻO ka maʻiʻo Cr kiʻekiʻe e loaʻa iā ia ka maikaʻi o ke koʻikoʻi koʻikoʻi i ka hoʻoheheʻe ʻia ʻana i ka wai maʻemaʻe ma lalo o ke kūlana radiation. Paʻa arc, nani hana, maikai kahe o ka hao hehee, me ka maikai loa kuʻihao kaʻina hana.
KOMPONO KIMIKA:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T RULA | - | - | - | - | - | - | - | - | - | - |
| NA RULA AWS | 0.04 | 1.00 | 0.50 | 28.0-31.5 | Ua haʻi aku ʻo Rem | 0.50 | 7.0-11.0 | 0.5-1.0 | 0.02 | 0.015 |
| KA WAIWAI LA'ANA | 0.028 | 0.15 | 0.11 | 29.8 | 59.03 | 0.06 | 9.8 | 0.86 | 0.001 | 0.002 |
WAIWAI MECHANICAL:
| WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | Hoʻomaʻamaʻa wela | ||||||
| GB/T RULA | - | - | - | - | - | ||||||
| NA RULA AWS | - | - | - | - | - | ||||||
| KA WAIWAI LA'ANA | - | 760 | 133/Ke wela lumi | 37 | 607°C*25h | ||||||