Nā mea hoʻoheheʻe nikela TIG ERNiCrMo-3 Mea kūʻai
KOMPONO KIMIKA:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T RULA | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| NA RULA AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0.015 |
| KA WAIWAI LA'ANA | 0.006 | 0.15 | 0.12 | 22.02 | 64.84 | 8.75 | 0.18 | 3.49 | 0.001 | 0.001 |
WAIWAI MECHANICAL:
| WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | ||||
| GB/T RULA | - | - | - | - | ||||
| NA RULA AWS | - | - | - | - | ||||
| KA WAIWAI LA'ANA | - | 790 | 159/-196 | 46 | ||||
Nickel-chromium-molybdenum nickel-base alloy kinoea welding uea, nominal haku mele 61% Ni-22% Cr-9% Mo-3.5% Nb + Ta.
Loaʻa i ka metala hoʻoheheʻe ʻia nā waiwai mechanical maikaʻi a me ke kūpaʻa maikaʻi i ka pitting corrosion a me ka crevice corrosion.
Paʻa arc, nani hana, maikai kahe o ka hao hehee, me ka maikai loa kuʻihao kaʻina hana.
KOMPONO KIMIKA:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T RULA | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.0-4.2 | - | - |
| NA RULA AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58 | 8.0-10.0 | 5.0 | 3.15-4.15 | 0.02 | 0.015 |
| KA WAIWAI LA'ANA | 0.006 | 0.15 | 0.12 | 22.02 | 64.84 | 8.75 | 0.18 | 3.49 | 0.001 | 0.001 |
WAIWAI MECHANICAL:
| WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | ||||
| GB/T RULA | - | - | - | - | ||||
| NA RULA AWS | - | - | - | - | ||||
| KA WAIWAI LA'ANA | - | 790 | 159/-196 | 46 | ||||