KOMPONO KIMIKA:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Ti | P | S |
GB/T RULA | 0.15 | 1.00 | 0.70 | - | ≥92 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
NA RULA AWS | 0.15 | 1.00 | 0.75 | - | ≥93 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
KA WAIWAI LA'ANA | 0.005 | 0.48 | 0.26 | 0.46 | 94.69 | 0.001 | 0.07 | 2.95 | 0.001 | 0.001 |
WAIWAI MECHANICAL:
WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | ||||
GB/T RULA | - | - | - | - | ||||
NA RULA AWS | - | - | - | - | ||||
KA WAIWAI LA'ANA | - | 550 | 276/-196 | 36 |
Maʻemaʻe nickel kinoea welding uwea, nominal haku mele 96% Ni-3% Ti.
Ma muli o ka hoʻohui ʻana o ka mea Ti pono, hiki ke hoʻemi maikaʻi ʻia ka porosity i ke kaʻina hana kuʻi.
Paʻa arc, nani hana, maikai kahe o ka hao hehee, me ka maikai loa kuʻihao kaʻina hana.
-
37,000 tona moku ukana nui
-
JU2000E pahu wili wili
-
Pahu hoʻoheheʻe palekana
KOMPONO KIMIKA:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Ti | P | S |
GB/T RULA | 0.15 | 1.00 | 0.70 | - | ≥92 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
NA RULA AWS | 0.15 | 1.00 | 0.75 | - | ≥93 | - | 1.0 | 2.0-3.5 | 0.03 | 0.015 |
KA WAIWAI LA'ANA | 0.005 | 0.48 | 0.26 | 0.46 | 94.69 | 0.001 | 0.07 | 2.95 | 0.001 | 0.001 |
WAIWAI MECHANICAL:
WAIWAI | IKAIKA HUA(MPa) | KA IKAIKA HOU (MPa) | KA WAIWAI IMAPACT J/℃ | ELONGATION(%) | ||||
GB/T RULA | - | - | - | - | ||||
NA RULA AWS | - | - | - | - | ||||
KA WAIWAI LA'ANA | - | 550 | 276/-196 | 36 |